Finger Break Out

Finger break out Mad e of cross linked polyolefin, inner coated with adhesive at the ends Provide sealing protection over 6-core cable crutch for variable frequency cable, trailing cable telecommunication cables, control cable, etc. Continuous operation temperature: -45℃ to 105℃ Shrink...

Product Details

Finger break out

Made of cross linked polyolefin, inner coated with adhesive at the ends

Provide sealing protection over 6-core cable crutch for variable frequency cable, trailing cable telecommunication cables, control cable, etc.

Continuous operation temperature: -45℃ to 105℃

Shrink temperature: start at 110℃, and fully recovered at 135℃


Heat Shrink special 6-cores Breakout


1.png


Technical Data

Property

Test Method

Standard Value

Operation Temperature

IEC 216

-45 to 105℃

Tensile Strength

ASTM-D-2671

≥12MPa

Elongation at Break (120℃,168 hrs)

ASTM-D-2671

≥300%

Tensile Strength after Aging (120℃,168 hrs)

ASTM-D-2671

≥10MPa

Elongation at Break after Aging

ASTM-D-2671

≥230%

Dielectric Strength

IEC 60243

≥20kV/mm

Water Absorption

ISO 62

≤0.5%

Volume R esistivity

IEC 60093

≥1014Ω.cm